AMBIENTUM BIOETHICA BIOLOGIA CHEMIA DIGITALIA DRAMATICA EDUCATIO ARTIS GYMNAST. ENGINEERING EPHEMERIDES EUROPAEA GEOGRAPHIA GEOLOGIA HISTORIA HISTORIA ARTIUM INFORMATICA IURISPRUDENTIA MATHEMATICA MUSICA NEGOTIA OECONOMICA PHILOLOGIA PHILOSOPHIA PHYSICA POLITICA PSYCHOLOGIA-PAEDAGOGIA SOCIOLOGIA THEOLOGIA CATHOLICA THEOLOGIA CATHOLICA LATIN THEOLOGIA GR.-CATH. VARAD THEOLOGIA ORTHODOXA THEOLOGIA REF. TRANSYLVAN
|
|||||||
Rezumat articol ediţie STUDIA UNIVERSITATIS BABEŞ-BOLYAI În partea de jos este prezentat rezumatul articolului selectat. Pentru revenire la cuprinsul ediţiei din care face parte acest articol, se accesează linkul din titlu. Pentru vizualizarea tuturor articolelor din arhivă la care este autor/coautor unul din autorii de mai jos, se accesează linkul din numele autorului. |
|||||||
STUDIA CHEMIA - Ediţia nr.2, Tom II din 2019 | |||||||
Articol: |
SINTERING AND CHARACTERIZATION OF NEW FORSTERITE CERAMICS. Autori: MARIA GOREA, MARIETA-ADRIANA NAGHIU, ALEXANDRA AVRAM, IOAN PETEAN, MARIA TOMOAIA-COTISEL. |
||||||
Rezumat: This study presents the sintering of new forsterite ceramics (FCs) using nano forsterite powder, obtained by a sol-gel method. The forsterite ceramics were sintered between 1200 and 1450°C. The resulted forsterite ceramics, namely FC at sintering temperature, T, written as FC(T), were characterized by various methods, XRD, AFM, apparent density, porosity and shrinkage. Mechanical properties were determined for FC(1400), with a Young elastic modulus at about 43.84 GPa and nano-indentation hardness at around 3.07 GPa. Furthermore, the in vitro biocompatibility of FC(1200) was evaluated using cell staining with fluorescein diacetate, FDA, assay. The cell viability results confirmed that forsterite ceramic, FC(1200), promotes cell adhesion and proliferation in cell culture, with no significant cytotoxic effects. These findings strongly recommend the new forsterite ceramics, as potential biomaterials for biomedical applications. Keywords: forsterite ceramics, porosity, density, biocompatibility |
|||||||
![]() |
|||||||
![]() |