The summary of the selected article appears at the bottom of the page. In order to get back to the contents of the issue this article belongs to you have to access the link from the title. In order to see all the articles of the archive which have as author/co-author one of the authors mentioned below, you have to access the link from the author's name.

 
       
         
    STUDIA CHEMIA - Issue no. 1 / 2016  
         
  Article:   OPTIMAL CONDITIONS FOR PREPARING CIGS THIN FILM THROUGH TWO-STEPPROCESS OF SPUTTERING FOLLOWED BY SELENIZATION.

Authors:  .
 
       
         
  Abstract:   Cu(In,Ga)Se2 films were prepared via a sputtering route followed by a selenization process, on glass substrates. Having a layer sequence Mo/In/Cu-Ga with preferred thicknesses, the metallic layers were selenized at vacuum of 6×10-3 mbar and 1 atm pressure with a total gas inlet of 7 sccm. Under vacuum, only single-phase CIGS was observed while at 1 atm, other phases in addition to CIGS were formed. The metallic layers were selenized at several temperatures. Pure-phased CIGS films were obtained by selenization at 600˚C. The crystallinity of the obtained films was further enhanced by increasing the selenization temperature. The produced CIGS films were studied by X-ray diffraction (XRD), scanning electron microscope (SEM) and energy dispersion spectroscopy (EDS) techniques.

Keywords: Cu(In,Ga)Se2 thin film, sputtering, selenization.
 
         
     
         
         
      Back to previous page