AMBIENTUM BIOETHICA BIOLOGIA CHEMIA DIGITALIA DRAMATICA EDUCATIO ARTIS GYMNAST. ENGINEERING EPHEMERIDES EUROPAEA GEOGRAPHIA GEOLOGIA HISTORIA HISTORIA ARTIUM INFORMATICA IURISPRUDENTIA MATHEMATICA MUSICA NEGOTIA OECONOMICA PHILOLOGIA PHILOSOPHIA PHYSICA POLITICA PSYCHOLOGIA-PAEDAGOGIA SOCIOLOGIA THEOLOGIA CATHOLICA THEOLOGIA CATHOLICA LATIN THEOLOGIA GR.-CATH. VARAD THEOLOGIA ORTHODOXA THEOLOGIA REF. TRANSYLVAN
Rezumat articol ediţie STUDIA UNIVERSITATIS BABEŞ-BOLYAI
În partea de jos este prezentat rezumatul articolului selectat. Pentru revenire la cuprinsul ediţiei din care face parte acest articol, se accesează linkul din titlu. Pentru vizualizarea tuturor articolelor din arhivă la care este autor/coautor unul din autorii de mai jos, se accesează linkul din numele autorului.
Autori: SORINA BORAN, GIANNIN MOȘOARCĂ, SABINA NITU, COSMIN VANCEA.
DOI: 10.24193/subbchem.2021.1.08
Published Online: 2021-03-20
Published Print: 2021-03-30
pp. 105-113
VIEW PDF
FULL PDF
ABSTRACT: The aim of this paper was the synthesis of some citric esters with potential biodegradable properties and their use as plasticizers or PVC lubricants. Citric esters were obtained in a bubbling column-type esterification reactor, using citric acid as the acid component, and monoethylene glycol, n-butanol, t-butanol as the hydroxyl components. The esters were characterized by FT-IR spectrometry to reveal the existence of the esteric bonds. Esters present a good thermal stability. The TCS criterion shows a level of compatibility specific to secondary plasticizers. There is a similarity between the values of the tested compounds and the standard DOF regarding hardness. The breaking strength are better and the values of elongation at break are close to the considered standards. The esters prove a very good migration towards rubber and are comparable to tribological fluids. The four balls test showed that without additives and at a test level of 40 daN for 60 min time period, the diameters of the wear spot are generally very good, being in the range of 0.43-0.62 mm. By adding oils, their behavior improves. The welding load values are also good (200-220 daN). The synthesized citrus esters have clear characteristics of plasticizers and/or lubricants for PVC.
Key words: citrus esters, bubble column reactor, plasticizer, lubricant